In view of the deficiencies of the prior art, Guangdong Yueluo Hardware Industry Co., Ltd. provides a relatively simple screw that can be manually disassembled. In order to achieve the above purpose, Guangdong Yueluo Hardware Industry Co., Ltd. provides the following technical scheme: a screw that can be disassembled manually, including a stud and a nut, and the axial direction of the screw is provided with a screw extending from the nut to the stud. A groove, a control column that is slidably matched with the groove is arranged in the groove, a through groove is opened on the circumferential side wall of the control column, and a circumferential side wall of the control column is provided with a parallel to the axis of the control column. A limit bar, the side wall of the groove is provided with a limit groove that cooperates with the limit bar, the control column is provided with a accommodating groove, and the accommodating groove is provided with a rotating rod that cooperates with the through groove, so The accommodating groove and the rotating rod are arranged separately. Further, a accommodating groove is opened at the corresponding groove on the nut, a baffle is hinged on the side wall of the accommodating groove, and a torsion spring is provided at the hinged joint between the baffle and the accommodating groove.
1. The twisted screw should be considered according to the actual inner diameter of the barrel, and the outer diameter deviation of the new screw should be given according to the normal clearance with the barrel. 2. After the thread surface with the reduced diameter of the worn screw is treated, the wear-resistant tungsten carbide alloy is thermally sprayed, and then ground to size. 3. Surfacing wear-resistant tungsten carbide alloy on the thread part of the worn screw. According to the degree of screw wear, surfacing welding is 1~2mm thick, and then the screw is ground and processed to size. This wear-resistant tungsten carbide alloy is composed of materials such as C, Cr, Vi, Co, W and B, which increases the wear resistance and corrosion resistance of the screw. 4. The bottom diameter of the screw is repaired by electroplating hard chromium. Chromium is also a wear-resistant and corrosion-resistant metal, but the hard chromium layer is easier to fall off.
At present, during assembly of many pin installation mechanisms, the pins need to be installed into the holes or arranged in an orderly manner, and there are many problems in this assembly method. First of all, during assembly, if the hole diameter of the hole product is large, when the pin enters the hole of the hole product, part of the pin entering the hole of the hole product is not fixed, which often leads to slight deviation. In addition, this assembly method is usually only suitable for parts with large apertures and small depths, and when installing multiple pins, it is impossible to automatically install all pins in place due to space constraints. Special tools need to be made for installation operations, and it is easy to cause pins. damage.
In the prior art, there are two ways to feed the screws of the locking screw machine, the air blowing type and the air suction type. The air suction type is suitable for relatively small screws. If the screw size is larger than M2, smaller than M5, and the length-diameter ratio is larger than 1.4, the air-blown screw machine can be selected.
In the manufacture of fasteners, the correct selection of fastener materials is an important part, because the performance of fasteners is closely related to its materials. If the material is improperly or incorrectly selected, the performance may not meet the requirements, the service life may be shortened, or even accidents or processing difficulties may occur, and the manufacturing cost will be high. Therefore, the selection of fastener materials is a very important link. Cold heading steel is a steel for fasteners with high interchangeability produced by cold heading forming process. Because it is formed by metal plastic processing at room temperature, each part has a large amount of deformation and a high deformation speed. Therefore, the performance requirements of cold heading steel raw materials are very strict. On the basis of long-term production practice and user research, combined with GB/T6478-2001 Technical Conditions for Cold Heading and Cold Extrusion Steel GB/T699-1999 High-Quality Carbon Structural Steel and target JISG3507-1991 Cold Heading Characteristics of Carbon Steel Wire Rod for Steel, taking the material requirements of grade 8.8 and grade 9.8 bolts and screws as an example, the determination of various chemical elements. If the C content is too high, the cold formability will be reduced; if it is too low, the mechanical properties of the parts cannot be met, so it is set at 0.25% - 0.55%. Mn can improve the permeability of steel, but adding too much will strengthen the matrix structure and affect the cold forming performance; when the part is quenched and tempered, it has the tendency to promote the growth of austenite grains, so it should be appropriately improved on the basis of international standards. 0.45 % - 0.80 %. Si can strengthen the ferrite and reduce the cold formability. SP is an impurity element, and their existence will cause segregation along the grain boundary, resulting in the embrittlement of the grain boundary and damage to the mechanical properties of the steel. It should be reduced as much as possible. B. The maximum value of boron content is 0.005%, because although boron element can significantly improve the permeability of steel, it will also increase the brittleness of steel. Excessive boron content is very unfavorable for workpieces such as bolts, screws and studs that require good comprehensive mechanical properties.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: PA66 nylon plastic cap nuts, countersunk head rivets, hexagonal nuts, groove nuts and other products, we can provide you with suitable for your products. Fastener Solutions.
The above content is uploaded by Yueluo or the Internet. If there is any copyright issue, please contact [email protected].