The fastener with a nut is composed of a polygonal nut and a bolt. The bolt includes an integral screw rod and a screw head. The fastening surfaces of the nut and the screw head are polygonal. There are external threads on the periphery of the screw, and the main point is that the axial three-dimensional shape of the nut and the screw head is an odd-numbered truncated cone, and the odd-numbered angle is an arc angle, and each arc angle corresponds to an elastic surface.

Riveting is a method for combining two pieces of metal. Therefore, riveting technology is often used to fasten rivets such as nuts or rivets to metal sheets.

series of nuts are known in the prior art, generally comprising an internal thread which can be threaded onto the external thread of a screw of corresponding design, or a threaded bolt. Nuts of the described type are used, for example, as nuts for fastening screw-like cable connections in conduits of sheet metal housings. Sheet metal housings of this type typically have walls so thin that they cannot be threaded, so a threaded connection of this type is required to complete the installation.

Stud bolts generally need to be surface treated. There are many types of bolt surface treatments. Generally, electroplating, blackening, oxidation, phosphating, and electroless zinc flake coating are commonly used. However, electroplated fasteners account for a large proportion of the actual use of fasteners. Especially in automobiles, tractors, home appliances, instrumentation, aerospace, communications and other industries and fields are more widely used. However, for threaded fasteners, not only a certain anti-corrosion capability is required in use, but also the interchangeability of threads must be ensured, which can also be called screwability here. In order to meet the dual-use performance of anti-corrosion and interchangeability required by threaded fasteners in use, it is very necessary to formulate special plating standards. GB/T5267.1-2002 [Threaded fastener electroplating layer] standard is one of the national standards fastener surface treatment series of standards, the standard includes: GB/T5267.1-2002 [fastener electroplating layer]; GB/T5267.2-2002 [Electrolytic zinc flake coating for fasteners] Two standards. This standard is equivalent to the international standard ISO4042; 1999 [Threaded fastener electroplating layer]. This standard replaces the GB/T5267-1985 [Threaded Fastener Electroplating Coating] standard.

The pretreatment process is a key process that determines the quality of nickel-phosphorus plating on high-strength bolts. The purpose of this process is to remove the passivation layer on the surface of the bolt and prevent the regeneration of the passivation film. The execution of this process directly determines the degree of bonding between the substrate and the coating. Most of the quality accidents in production are caused by poor pretreatment of bolts. Before plating, the oil, rust and oxide scale attached to the surface of the bolt must be carefully removed; the difference with electroplating is that it should be inspected more carefully, and plating is absolutely not allowed on unclean bolts. ① Inspection of bolts: Visual inspection of the surface quality of bolts requires that any burrs left by processing must be removed, and sharp edges and corners must be rounded. ② Manual degreasing; ensure that the surface of the substrate is free of oil stains. ③ Soak and remove oil; boil the bolts in alkaline water to remove the surface oil. ④ Pickling: In order to prevent the alkaline degreasing solution from contaminating the flash nickel plating tank, electro-activation treatment is carried out with pickling solution before flash nickel plating. ⑤ Electro-activation; electro-activation treatment with acid solution. ⑥ Flash nickel plating; flash nickel plating should be used for low alloy steel to increase the bonding strength between the coating and the substrate.

We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: natural hex bolts, GB3788U screws, cup head flat spring washer combination bolts, left tooth inverted external hexagon anti-thread bolts and other products, we can provide You have the right fastener solution for you.

Hexagonal standoff

Customized BSO blind hole pressure riveting stud


The above content is uploaded by Yueluo or the Internet. If there is any copyright issue, please contact [email protected].